PVC PIPES


A FEW WORDS ABOUT PVC AS A PIPE MATERIAL


Of all the plastic materials available for piping systems PVC has been found to all possess the best combination of properties and economy. Poly Vinyl Chloride (PVC) is a thermoplastic used and approved worldwide as a dependable engineering material. PVC pipes are produced by mixing PVC resin (a petro-chemical product) with stabilizers, lubricants, pigments, fillers, processing aids and plasticizers

'Hari Plaast' PVC PIPES & FITTINGS are manufactured conforming to various Indian & International standards like IS : 4985 , IS : 12818, ASTM- D- 1785, BS, DIN and ISO in various sizes ranging upto 315 mm in diameter in all classes and pressure rating.

It produces PVC pipes for every conceivable applications from drinking water supply and bore well systems to transportation of abrasive slurries.

“Hari plaast” RIGID PVC PIPES FOR SOLVENT CEMENT AS WELL AS ELASTOMERIC RUBBER RING JOINTING


These pipes are manufactured in accordance with Bureau of Indian Standards Specification IS: 4985-2000 and ISO 4422 in various sizes ranging upto 315 mm in all classes and pressure ratings.

“Hari plaast” PVC CASING PIPES CONFORMING TO IS: 12818-1992


These pipes are manufactured as per BIS 12818-1992 and supplied in 2, 3 & 4 meters length with one end having male threads & the other end having female threads. Threads are V or trapezoids type and protection caps are provided on the threads to protect the threads in transit. Two types of pipes i.e. Shallow Well (C.S.) and Medium Well (C.M.) are available.

Hari plaast” RIBBED SCREEN PIPES CONFORMING TO IS: 12818-1992


Hari Plaast PVC Ribbed Screen pipes have longitudinal ribs and transverse slots. These pipes are generally used in combined wells where normal Screen pipes does not work. These pipes carries BIS Certification mark and manufactured in lengths 1, 2, & 3 meters with one end having male threads and the other end having female threads. The slot width range for screens is 0.2mm,0.3mm,0.5mm,0.75mm,1.0mm,2.0mm & 3.0mm.

“Hari plaast” PVC PLUMBING AND CASING PIPES MADE TO ASTM D 1785.


These pipes are manufactured as per ASTM D 1785 and supplied in 3, 5 & 6 meters length with one end having male threads & the other end having female threads. These pipes are well accepted by the users everywhere for plumbing, water distribution and particularly in deep tube well connection because of higher collapse strength.

“Hari plaast” SWR drainage system:


“Hari plaast” SWR pipes are manufactured in accordance with BIS specn No. IS: 13592 and are utilized in applications such as laboratory, chemical lines, overflow and waste discharge systems in chemical plants, waste lines in the food processing industry and effluent discharge in diary plants other than domestic drainage systems. Hari Plaast SWR pipes are available in 2,4,6 & 10 feet length in the range of 75, 110 and 160 mm OD.

BENEFITS OF “Hari plaast” PVC PIPE:


Long life, Non corrosive, Light weight, Continuous flow, Cost effective, Low electric cost, Easy to Install, repair & replace, Hygienic water supply, Non conductor to heat and electric, Prevent bacterial growth and resistance to chemical.

FIELD OF APPLICATIONS:


Domestic

Plumbing & Drainage applications in homes, offices, hotels, residential complexes, commercial complexes etc.

Industrial

Industrial process lines. & R.O (Raverse Osmosis) / Water purifier plants. Salt water line. Aggressive fluid transportation. Sugar, paper and distillery. Coal washing and ash handing.

Others:

Water distribution lines and bore well applications.

PROPERTIES OF PVC


GENERAL TEST METHOD   UNIT
Cell Classification ASTM D1784 12454-B --
Maximum Service Temperature (uPVC) -- 60 °C
Specific @ Gravity 73° F (uPVC)

ASTM D792

1.44+0.03 --
Water Absorption in 24 hrs @77° F

ASTM D570

0.05 % weight increment
Hardness, Rockwell

ASTM D785

110-120 --
Hardness, Durometer D

ASTM D2240

80+3 --
Hazen-Williams Factor

--

C=150 --
MECHANICAL      
Tensile Strength @73° F ASTM D638 >48.3 MPa
Tensile Modulus of Elasticity @73
° F
ASTM D638 >2758 MPa
Flexural Strength @ 73° F ASTM D790 14450 psi
Compressive Strength @ 73° F (min) ASTM D695 9600 psi
Izod Impact, notched @73° F ASTM D256 <0.65 ft-lb/in
Hydrostatic Desing Stress ASTM D1785 2000 Psi
THERMAL      
Coefficient of Linear Expansion ASTM D696 209x10-5 In/in°F
Coefficient of Thermal Conductivity ASTM C177 3.5x10-4 (Cal)(cm)(cm2)(sec)(°C)
Heat Deflection Temp under load,      
Annealed @1.82 MPa ASTM 648 >70 °C
Specific Heat ASTM D2766 0.25 Cal / (gm°C)
Vicat Softening Temperature (uPVC) IS 4985 >80 °C
FIRE PERFORMANCE      
Limiting Oxygen Inbox (L.O.I.) ASTM D2863 43 %
Average Extent of Burning ASTM D635 <25 mm
Average Time of Burning' ASTM D635 <10 sec